Polyolefine - SPLT
 Low Shrink Temperature Flame Retarded Heat Shrinkable Polyolefin Tubing
Shrink Ratio:
2 : 1
Operating Temperature:
-40°C to +125°C
Shrink Temperature:
+80°C
Remark:
Suitable for use with components that are sensative to heat
Standard Colours:
Black and clear. Other colours available to order
Standard Packaging:
On reels
To order:
specificy product number, size and color(example SPLT 4,8 black).
Legenda:       
|
|
|
| Property |
Test method |
Values |
| Tensile Strength |
ISO 37 |
10 Mpa (min.) |
| Ultimate Elongation |
ISO 37 |
200% (min.) |
| Heat Shock |
ASTM D2671
(4 hrs at 200°C) |
no dripping,
cracking or flowing |
| Heat Ageing |
ISO 188
(168 hrs at 150°C) |
|
Heat Ageing
Ultimate Elongation) |
ISO 37 |
150% (min.) |
| Recovery at +80°C |
|
50% (min.) |
| Low Temperature Flexibilty |
ASTM D2671
(4 hrs at -45°C) |
no cracking |
Flammability
(except Clear) |
MVSS-302 |
pass |
| Electric Strength |
IEC 243-1 |
15KV/mm (min.) |
Corrosion
(Copper Mirror) |
ASTM D2671 |
no corrosion |
| Fluid Resistance |
ISO 1817 |
|
Fluid Resistance
Tensile Strength |
ISO 37 |
5Mpa (min.) |
Fluid Resistance
Ultimate Elongation |
|
175% (min.) |
| Type |
Shrinktek |
Militairy |
Underwriters lab |
CSA |
| SPLT |
ST6004 |
|
|
|
| Ordering size |
Min. expansion |
Max. shrink |
Nom. recovered
wall |
Standard length |
| mm |
mm |
mm |
mm |
m |
| 1.2 |
1,2 |
0.6 |
0.33 |
150 |
| 1,6 |
1,6 |
0,8 |
0,33 |
150 |
| 2,4 |
2,4 |
1,2 |
0,44 |
150 |
| 3,2 |
3,2 |
1,6 |
0,44 |
150 |
| 4,8 |
4,8 |
2,4 |
0,44 |
75 |
| 6,4 |
6,4 |
3,2 |
0,56 |
75 |
| 9,5 |
9,5 |
4,8 |
0,56 |
75 |
| 12,7 |
12,7 |
6,4 |
0,56 |
75 |
| 19 |
19,1 |
9,5 |
0,69 |
60 |
| 25,4 |
25,4 |
12,7 |
0,77 |
60 |
| 38,1 |
38,1 |
19 |
1 |
30 |
| 50,8 |
50,8 |
25,4 |
1,15 |
30 |
|