Polyolefine - SE
 Abrasion Resistant Flexible Flame Retarded Heat Shrinkable Elastomer Tubing
Shrink Ratio:
2:1
Operating Temperature:
range -70°C to +120°C
Shrink Temperature:
-100°C
Remark:
Ideal for providing a mechanically tough, solvent resistant cable jacket
Standard Colours:
Black. Other colours not presently available
Standard Packaging:
on reels (see table for lengths)
To order:
specify product part number, size and colour (e.g. SE 6.4 BLK)
Legenda:   
|
|
|
| Property |
Test method |
Values |
| Tensile Strenght |
ISO 37 |
14 Mpa (min.) |
| Ultimate Elongation |
ISO 37 |
350% (min.) |
| Heat Shock |
ASTM D2671 (4 hrs. at +200°C) |
no dripping,
cracking or flowing |
| Heat Ageing |
ISO 188 (168 hrs. at 150°C) |
|
| Heat Ageing (Tensile Strength) |
ISO 37 |
10 Mpa (min.) |
| Heat Ageing(Ultimate Elongation) |
|
200% (min.) |
| Low Temperature Flexibility |
ASTM D2671 (4 hrs. at -75°C) |
no cracking |
| Flammability |
ASTM D876 |
pass |
| Electric Strength |
IEC 243-1 |
8KV/mm (min.) |
Corrosion
(Copper Contact and Copper Mirror) |
ASTM D2671 |
no corrosion |
Fluid Resistance
Gasoline,Hydraulic Fluid
Lubricating Oil |
ISO 1817 |
|
| Fluid Resistance (Tensile Strenght) |
ISO 37 |
10 Mpa (min.) |
| Fluid Resistance (Ultimate Elongation) |
|
200% (min.) |
| Fungus Resistance |
BS 2011 Pt 2.1j |
Not greater than rating 2 |
| Type |
Shrinktek |
Militairy |
Underwriters lab |
CSA |
| SE |
ST6010 |
MIL-DTL 23053/16 |
|
|
| Ordering size |
Min. expansion |
Max. shrink |
Nom. recovered
wall |
Standard length |
| mm |
mm |
mm |
mm |
m |
| 3.2 |
3,2 |
1.6 |
0.76 |
50 |
| 4,8 |
4,8 |
2,4 |
0,84 |
50 |
| 6,4 |
6,4 |
3,2 |
0,89 |
50 |
| 9,5 |
9,5 |
4,8 |
1,02 |
50 |
| 12,7 |
12,7 |
6,4 |
1,22 |
30 |
| 19 |
19 |
9,5 |
1,45 |
30 |
| 25,4 |
25,4 |
12,7 |
1,78 |
30 |
| 31,8 |
31,8 |
18,1 |
2,2 |
30 |
| 38 |
38 |
19,1 |
2,41 |
15 |
| 50,8 |
50,8 |
25,4 |
2,79 |
22 |
|