Nederlands
Polyolefine - Viton
 Abrasion & Chemical Resistant Viton Heat Shrinkable Tubing.
Shrink Ratio:
2:1
Operating Temperature:
-55°C to +200°C
Shrink Temperature:
+175°C
Remark:
Resistance to fuels, lubricants, acids and solvents at high temperatures makes it suitable for many varied applications
Standard Colours:
Black
Standard Packaging:
on reels.
To order:
specify product number, size and color (for example Viton 3,2 black).
Legenda:    
|
|
|
| Property |
Test method |
Values |
| Tensile Strength |
ISO 37 |
10.3 Mpa (min.) |
| Ultimate Elongation |
ISO 37 |
250% (min.) |
| Specific Gravity |
ISO 1183 |
1,95 (max.) |
| Heat Shock |
ASTM D2671 (4 hrs
at +300°C) |
no dripping,
cracking or flowing |
| Heat Ageing |
ISO 188 (168 hrs
at 250°C) |
|
Heat Ageing
(Ultimate Elongation) |
ISO 37 |
200% (min.) |
| Low Temperature Flexibility |
ASTM D2671 (4 hrs
at -55°C) |
no cracking |
| Flammability |
ASTM D876 |
pass |
| Electric Strength |
IEC 243-1 |
6KV/mm (min.) |
Corrosion (Copper Contact
and Copper Mirror) |
ASTM D2671 |
no corrosion |
| Water Absorption |
ISO 62 |
0,5% (max.) |
| Fluid Resistance |
ISO 1817 |
|
Fluid Resistance
(Tensile Strength) |
ISO 37 |
8,8 Mpa (min.) |
Fluid Resistance
(Ultimate Elongation) |
|
200% (min.) |
Fluid Resistance
(Ultimate Elongation) |
|
250% (min.) |
| Fungus Resistance |
ISO 846 |
no fungal growth |
| Type |
Shrinktek |
Militairy |
Underwriters lab |
CSA |
| Viton |
ST6011 |
MIL-DTL 23053/16,
DEF STAN 59-97 type 4A,
VG 95343 Pt5,
MILR 46846 type 11 |
|
|
| Ordering size |
Min. expansion |
Max. shrink |
Nom. recovered
wall |
Standard length |
| mm |
mm |
mm |
mm |
m |
| 3,2 |
3,2 |
1,6 |
0,8 |
50 |
| 4,8 |
4,8 |
2,4 |
0,9 |
50 |
| 6,4 |
6,4 |
3,2 |
0,9 |
50 |
| 9,5 |
9,5 |
4,8 |
1 |
25 |
| 12,7 |
12,7 |
6,4 |
1,2 |
25 |
| 19,1 |
19,1 |
9,5 |
1,4 |
25 |
| 25,4 |
25,4 |
12,7 |
1,8 |
25 |
| 38,1 |
38,1 |
19 |
2,4 |
15 |
| 50,8 |
50,8 |
25,4 |
2,8 |
15 |
|
Legenda
 Domestic  Automotive Electrical Computing  Military Aviation  Industrial Transport
|