Heat shrinkable tubing

SPLT

Low Shrink Temperature Flame Retarded Heat Shrinkable Polyolefin Tubing

 

Shrink Ratio:
2 : 1

 

Operating temperature:
-40°C to +125°C

 

Shrink temperature:
+80°C

 

Remark:
Suitable for use with components that are sensative to heat

 

Standard colours:

Black and clear. Other colours available to order

 

Standard packaging:
On reels

 

To order:
Specificy product number, size and color(example SPLT 4,8 black).

Suitable for:

Domestic Electrical Computing Aviation Industrial Transport
Back
Specific values
References / approvals
Ordering data

Specific values

Property

Test method

Values

Tensile Strenght

ISO 37

10 Mpa (min.)

Ultimate Elongation

ISO 37

200% (min.)

Heat Shock

ASTM D2671 (4 hrs. at +200°C)

no dripping, cracking or flowing

Heat Ageing

ISO 188 (168 hrs. at 150°C)

Heat Ageing(Ultimate Elongation)

ISO 37

150% (min.)

Recovery at +80°C

50% (min.)

Low Temperature Flexibility

ASTM D2671 (4 hrs. at -45°C)

no cracking

Flammability (except Clear)

MVSS-302

pass

Electric Strength

IEC 243-1

15KV/mm (min.)

Corrosion (Copper Contact and Copper Mirror)

ASTM D2671

no corrosion

Fluid Resistance

ISO 1817

Fluid Resistance (Tensile Strenght)

ISO 37

5Mpa (min.)

Fluid Resistance (Ultimate Elongation)

175% (min.)

References / approvals

Type

Shrinktek

Military

Underwriters lab

CSA

SPLT

ST6004

Ordering data

Ordering

Min. expansion (mm)

Max. shrink (mm)

Nom. recovered wall (mm)

Standard length (m)

1.2

1.2

0.6

0.33

150

1.6

1.6

0.8

0.33

150

2.4

2.4

1.2

0.44

150

3.2

3.2

1.6

0.44

150

4.8

4.8

2.4

0.44

75

6.4

6.4

3.2

0.56

75

9.5

9.5

4.8

0.56

75

12.7

12.7

6.4

0.56

75

19

19.1

9.5

0.69

60

25.4

25.4

12.7

0.77

60

38.1

38.1

19

1

30

50.8

50.8

25.4

1.15

30